Applications of 8050 ECO for Filling & FairingApplications of 8050 ECO for Filling & Fairing

RESOLTECH 8050 ECO

Hardener 8058 ECO

Biobased epoxy profiling & fairing filler

  • 25% biobased on the resin part*
  • Simple mixing ratio 1/1 by weight or volume
  • Easy sanding
  • Fast curing
  • Lightweight: 0,8 density
    *ratio of the number of biobased carbon atoms / the number of total carbon atoms

RESOLTECH 8050 ECO / 8058 ECO is a fast curing, lightweight, and easy sanding epoxy filler.

It is a premium choice for profiling & fairing above and below the waterline for professional applicators on steel, aluminum and composite materials.

The specially formulated lightweight epoxy filler will apply from very thin layers up to 25 mm in one coat without the risk of sagging/slumping. This filler will result in a high strength and impact resistant watertight surface.

The formulation of the 8050 ECO / 8058 ECO will help improve health and safety for the workers and follows the latest EU regulation (CE) n°453/2010 and does not contain any CMR materials.

When sanded, the surface of this system is smooth enough to be directly overcoated with RESOLCOAT 3010T / 3014T high build epoxy primer and is compatible with all paints & primers.

RESOLTECH 8050 ECO / 8058 ECO fast curing characteristics enable applications of several layers a day with sanding between them, improving the productivity of the workers. It may be applied in covered facilities or outside as it offers little sensivity to climate conditions.

Its excellent waterproof property enables to guarantee long lasting barriers when used as osmosis treatment.

Easy to sand or mill with CNC, RESOLTECH 8050 ECO / 8058 ECO may be used as profiling filler on low density foams blocks for plugs manufacturing and tooling boards adhesive.

RESOLTECH 8050 ECO / 8058 ECO is the product that offers long-term performance of superior quality.

With 25% of biobased carbon atoms in the resin part, the use of 8050 ECO will reduce the carbon footprint of profiling & fairing making no concessions on thermo-mechanical performances.

Mix density
0.8
Gel time on 70 mL, 4cm at 23°C
18m
TG (°C)
68