Applications of 2010 for CastingApplications of 2010 for Casting

RESOLTECH 2010

Hardeners 2013 to 2019

Multipurpose Casting Epoxy System

  • Adjustable pot life from 13h45min to 15 min.
  • Room temperature cure & mould release.
  • Excellent air release properties.

Thanks to its low viscosity and low exothermy, this system enables casting by gravity or under vacuum, with the incorporation of any kind of fillers.

All hardeners mix with a 100:35 ratio by weight and can be pre-blended together to precisely adjust the desired potlife. It is possible to release the parts from the mould without post-curing. Most of the thermomechanical properties of the laminate will be obtained after 7 days at room temperature. Once cured, cast parts may be released from the moulds without post-cure. The greatest quality of the RESOLTECH 2010 / 2013 - 2019 system is its exceptional wetting properties and air release. This resin formulated with specific wetting agents will enable to add high amounts of all types of fillers, while providing good flowability during the casting.

TG (°C)
75
Mix density
1.11
Mix viscosity (mPa.s)
205 - 1,170
Gel time on 70 mL, 4cm at 23°C
15m - 10h