Applications of 1050T for Wet layupApplications of 1050T for Wet layup

RESOLTECH 1050T

Hardeners 1053S to 1059S

Structural lamination epoxy system

New hardeners salicylic acid free

  • Adjustable pot life from 10min to 14hours
  • Room temperature cure & mould release
  • TG up to 75°C
  • Excellent wetting properties on all reinforcements
  • For small to XXL size parts productions

The 1050 epoxy laminating system is formulated to manufacture high performance lightweight structures with glass, carbon, aramid and basalt reinforcements with or without post-curing.

This latest generation system, without CMR substances (including salicylic acid) according to GHS criteria is optimized with a low exotherm, low viscosity and excellent air release properties. This epoxy system is also suitable for the manufacture of small to very large structures and composite parts by wet lay-up, infusion, injection moulding or filament winding while guaranteeing low toxicity working conditions to the users.

All hardeners mix with a 100/35 ratio and can be pre-blended together to precisely adjust the desired pot life. The 1050 resin + 1053S system is particularly recommended for infusion thanks to its low mixed viscosity (205mPa.s).

The 1050 resin is available in a thixotropic version 1050T for wet lay-up application in vertical or overhanging surfaces prone to resin dripping.

It is possible to release the parts from the mould without post-curing. To speed up demoulding a 40ºC cure is possible and optimum thermo-mechanical properties of the laminate will be obtained after a 60ºC post-curing cycle.

Laminates produced with the 1050 system will offer very good mechanical properties combined with excellent fatigue resistance thanks to its exceptional wetting properties, improving the composite interlaminar properties even on aramid reinforcements.

Its elongation at break in flexion up to 5% makes the 1050 system as a prime choice epoxy system for large structural laminates submitted to dynamic working efforts.

TG (°C)
75
Mix density
1.1
Mix viscosity (mPa.s)
251 - 637
Gel time on 70 mL, 4cm at 23°C
10m - 14h