RESOLTECH 1070(S) CLEAR

Hardeners 1074 & 1077

Clear epoxy laminating system

  • New UV resistant formula (January 2019)
  • For structural laminates and topcoats
  • Ease of use, room temperature curing, self-leveling
  • Excellent degassing and wetting properties
  • Polyester topcoat application without inhibition
  • Three choices of reactivity

RESOLTECH 1070(S) CLEAR is a high end crystal clear epoxy laminating system formulated to produce clear laminates and high gloss clear coatings with good UV stability and high mechanical properties.


Thanks to its new formulation(January 2019), 1070(S) CLEAR is now the best available UV resistance resin on the market.

The 1070(S) CLEAR system is formulated for professionals who manufacture surf, wind-surfs, kite-boards, or any composites parts with high-end finish aspects requirements.

On white foams (polystyrene and PU) the additive Optical brightener (sold separately) greatly improves the white color of the board. Simply pour 1 to 3 drops of additive in 100g of resin in the topcoat (see details in datasheet).

The wetting out properties of this system and air release are acclaimed for and it has no sensitivity to blush. The resulting laminates will be absolutely clear on carbon fibre and even transparent if applied on special glass fabrics such as Hexcel TF970 treatment.

The viscosity is adapted for squeegee, or brush application, and provides a perfect bubble free surface due to its surface tension properties.

The system has been formulated in order to leave virtually no free amines on the laminate. This enables the use of any quality polyester topcoat for quick sanding on top of the laminate without inhibition of the polyester. RESOLTECH 1070(S) CLEAR will cure at room temperature, post curing will elevate the final TG like any other epoxy system.

TG (°C)
64
Mix density
1.1
Mix viscosity (mPa.s)
560 - 940
Gel time on 70 mL, 4cm at 23°C
15m - 3h